          LJ-SJ501
          Jinan Jincai Welding Material Co. , Ltd.

          Conforming to::GB /T5293  S43S0AR-SU08A      S49S2AR-SU26

          Equivalent to:  AWS-A5.17  F6A0-EL12  F7A2-EM12K

          DIN BAR 188AC10KM

          DESCRIPTION AND APPLICATIONS

          Agglomerated acid flux for welding of ordinary carbon manganese, low alloy structure and boiler quality steel in combination with appropriate SAW wire (such as EL8,EM12. EM12K). The flux suitable for high speed welding and provides very good weld bead appearance and excellent slag removal even with narrow groove and fillet welds. The other character of LJ-SJ501 is high resistance to cracking and porosity. Especially it is insensitive to oil, rust, scale and dirt on the surface to be welded. Most being applied to double-side with single pass weld and fillet welds. As the consumption of the flux is very low,it is very economical.

          • Flux type: Aluminum-Rutile

          • Basicity index: 0.5-0.8

          • Grain size:2.0-0.28mm(10-60meshes)

          Compositions of fluxes (%)

          SiO2+TiO2

          Al2O3+MnO

          CaF2

          S

          P

           25-35

          50-60

          3-10

          ≤0.035

          ≤0.04

          Typical all weld metal mechanical property

          Wire

          Yield Stress

          Tensile Strength

          Elongation

          AKV(J)

          EL12

          ≥330Mpa 

            415-550Mpa

          ≥22%

          ≥27/0℃

          EM12K

          ≥400Mpa

          480-650Mpa

          ≥22%

          ≥27/0℃

          Remark

          1.       Before welding, fluxes should be baked for two hours at 300-350℃.

          2.       Removal of rust, oil, dirt, water, impurities, etc in welding-areas.

           